GLASS TYPES




ORANGE
HEBO Schott Hoya
0 530 ~ OG 530
O 540 ~ O-54
O 550 ~ OG 550
O 565 ~ OG 570
O 580 ~ O-58


Orange Glass Characteristic

TypeThicknessn (587,8 nm)p (g/cm³)Tg(°C)Ts(°C)α × 10-7(°C)DADWBubblesHomogeneityStriae
0 5302 mm1,522,6452760510332211
O 5402 mm1,5232,6452760510332211
O 5502 mm1,5232,6452760510332211
O 5652 mm1,5232,6452760510332211
O 5802 mm1,5232,6452760510312211




TypeThicknessA(2856K)D65λt50 %(nm)λp (nm)p (%)Tk (nm/°C)
  xyY(%)xyY(%)    
0 5302 mm0,5490,44882,20,5040,49270,2530 ± 9620≥ 88,70,12
O 5402 mm0,5720,42772,90,5370,46159,3540 ± 9630≥ 88,70,13
O 5502 mm0,5940,40563,60,5690,43048,4550 ± 9640≥ 88,70,13
O 5652 mm0,6220,37751,60,6050,39536,7565 ± 9655≥ 88,70,14
O 5802 mm0,6580,34235,90,6490,35123,3580 ± 9680≥ 88,70,15